Anomalous ferromagnetic behaviour of the Y2O3 and CuO components in YBa2Cu3Oy (Y123) was observed after severe reduction of particle size. The particle size reduction was performed in following way: Y2O3, BaCO3 and CuO ...

The resistivity measurements of the Yb1-xGdxBa 2Cu3O7-y superconducting samples prepared by using the solid-state reaction technique for x=0.0, 0.2, 0.4, 0.6, 0.8 and 1.0 were performed in QD-PPMS system under different ...

To investigate the effect of x on c-lattice parameter, the activation energy, and the magnetic power constant of activation energy, the nominal composition of Y1-xYbx/2Gdx/2Ba2Cu3O7-y superconducting samples for x = 0.0, ...

The Y1-xYbx/2Gdx/2Ba2Cu3O7-y superconducting samples for x = 0.0, 0.2, 0.4, 0.6, 0.8 and 1.0 were prepared by using the solid-state reaction technique. Resistivity measurements of the samples were performed in QD-PPMS ...

The resistance transitions of Gd-diffused polycrystalline Y123 samples have been measured as a function of temperature and magnetic field. It is deduced from experimental results that the activation energy increases when ...

The Yb1-xGdxBa2Cu3O7-y superconducting samples (x = 0.0, 0.2, 0.4, 0.6, 0.8 and 1.0) which were prepared by solid-state reaction technique were studied to investigate the effect of x on c-lattice parameter, the activation ...

The effect of Yb diffusion on structural evolution and superconducting properties of YBa2Cu307-x (Y123) prepared in the bulk polycrystalline form were studied. The ytterbium (Yb) diffusion in superconducting Y123 ceramic ...

After the preparation of Sm123 and Yb211 by melt-powder-melt growth and solid-state-reaction, respectively, the nominal compositions of (Sm123) 1-x(Yb211) x for x = 0.00, 0.05, 0.10, 0.15, 0.20 and 0.25 were prepared to ...

Superconducting Y123 samples were prepared by the solid-state reaction (SSR) method. To get a layer of Yb (thickness ?4 ?m) on the surface of one side of the sample an ultrahigh-vacuum electron-beam deposition system was ...