Impact of an ultra-thin antimony layer on the performance of CdTe-based photodetectors under varying illumination conditions

Göster/Aç

Full Text / Tam Metin (4.620Mb)

Erişim

info:eu-repo/semantics/closedAccess

Tarih

2025

Yazar

Çiriş, Ali
Atasoy, Yavuz
Bayazıt, Tuğba
Küçükömeroğlu, Tayfur
Bacaksız, Emin

Üst veri

Tüm öğe kaydını göster

Künye

Çiriş, A., Atasoy, Y., Bayazıt, T., Küçükömeroğlu, T., & Bacaksız, E. (2025). Impact of an ultra-thin antimony layer on the performance of CdTe-based photodetectors under varying illumination conditions. Sensors and Actuators A: Physical, 394, 116884. https://doi.org/10.1016/j.sna.2025.116884

Özet

In this study, the impact of thin Sb-layer in the device on CdTe photodetector parameters were examined. CdTe films were deposited by the close spaced sublimation (CSS) method, and then Sb-thin films were grown onto CdTe coated substrates by DC sputtering. In the structural analyses, it was observed that both as-dep and annealed CdTe exhibited the formation of double phases (Cd-rich and Cd-poor CdTe). However, Sb coating on CdTe led to the formation of Cd-rich and stoichiometric cubic CdTe phases. Surface images revealed that all samples exhibited a densely-packed grain morphology, with average grain sizes of 7.74 µm, 8.15 µm, and 7.15 µm for as-dep. CdTe, annealed CdTe, and annealed CdTe/Sb, respectively. It was calculated that the preparation steps of the samples had no considerable effect on the bandgap, as all samples exhibited values within the range of 1.45–1.48 eV. Meanwhile, PL features in the range of 817–820 nm were observed for all samples, attributed to acceptor-bound exciton transitions in the as-dep CdTe, and to donor-bound exciton transitions in the annealed CdTe and CdTe/Sb films. All photodetectors exhibited photoconductive behavior; however, the best performance was achieved by annealing CdTe under Cd-overpressure (R=1.7 mA/W, D*=3.4 ×10⁷ Jones for blue light, and R=2.5 mA/W, D*=5 ×10⁷ Jones for red light). Furthermore, the annealed CdTe photodetector maintained a significant level of performance even after six months without encapsulation. In contrast, Sb coating on CdTe led to a slight degradation in device performance, attributed to its adverse effects on defect levels and grain structure.

Kaynak

Sensors and Actuators A: Physical

Cilt

394

Bağlantı

https://doi.org/10.1016/j.sna.2025.116884
https://hdl.handle.net/11436/10732

Koleksiyonlar

  • Merkezi Araştırma Laboratuvarı Uygulama ve Araştırma Merkezi Koleksiyonu [11]
  • Scopus İndeksli Yayınlar Koleksiyonu [6118]



DSpace software copyright © 2002-2015  DuraSpace
İletişim | Geri Bildirim
Theme by 
@mire NV
 

 




| Yönerge | Rehber | İletişim |

DSpace@RTEÜ

by OpenAIRE
Gelişmiş Arama

sherpa/romeo

Göz at

Tüm DSpaceBölümler & KoleksiyonlarTarihe GöreYazara GöreBaşlığa GöreKonuya GöreTüre GöreDile GöreBölüme GöreKategoriye GöreYayıncıya GöreErişim ŞekliKurum Yazarına GöreBu KoleksiyonTarihe GöreYazara GöreBaşlığa GöreKonuya GöreTüre GöreDile GöreBölüme GöreKategoriye GöreYayıncıya GöreErişim ŞekliKurum Yazarına Göre

Hesabım

GirişKayıt

İstatistikler

Google Analitik İstatistiklerini Görüntüle

DSpace software copyright © 2002-2015  DuraSpace
İletişim | Geri Bildirim
Theme by 
@mire NV
 

 


|| Rehber|| Yönerge || Kütüphane || Recep Tayyip Erdoğan Üniversitesi || OAI-PMH ||

Recep Tayyip Erdoğan Üniversitesi, Rize, Türkiye
İçerikte herhangi bir hata görürseniz, lütfen bildiriniz:

Creative Commons License
Recep Tayyip Erdoğan Üniversitesi Institutional Repository is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 4.0 Unported License..

DSpace@RTEÜ:


DSpace 6.2

tarafından İdeal DSpace hizmetleri çerçevesinde özelleştirilerek kurulmuştur.