Hf2Co11 thin films: Rare-earth-free permanent nanomagnets

Thumbnail

Göster/Aç

Full Text / Tam Metin (1.488Mb)

Erişim

info:eu-repo/semantics/closedAccess

Tarih

2017

Yazar

Yüzüak, Gizem Durak
Yüzüak, Ercüment
Elerman, Yalçın

Üst veri

Tüm öğe kaydını göster

Künye

Yüzüak, G.D., Yüzüak, E. & Elerman, Y. (2017). Hf2Co11 thin films: Rare-earth-free permanent nanomagnets. Thin Solid Films, 625, 115-121. https://doi.org/10.1016/j.tsf.2017.01.050

Özet

Hf2Co11 thin films were deposited on single crystalline Si(100) substrates by using conventional direct current (DC) magnetron sputtering with a Hf2Co11 alloy target. All films were grown at room temperature with 120W sputtering power. in order to obtain the composition of the desired, the working pressure was changed from 0.66 to 1.05 Pa. the relationships between structural and magnetic properties in Hf-Co films were studied by using differential thermal analyzer, glancing incidence X-ray diffraction, scanning electron microscopy, energy dispersive X-ray analysis, atomic force microscopy, magnetic force microscopy and vibrating sample magnetometer. It revealed that the as-deposited films were amorphous at room temperature for all deposition pressures and showed soft ferromagnetic phase. in order to increase the coercive field associated with an advancing transition to hard phase, thin films were post-annealed from 773 K to 973 K. Post-annealing process led to a high remanence magnetization and improved the squareness of the demagnetization curve. Their saturation magnetization values varied from 515 to 1378 kA/m and also coercive field values varied from 52x10(-4) to 153x10(-3) Tat room temperature depending on post-annealing temperatures. Hf2Co11 soft ferromagnetic phase was modified by formation of post-annealing and was given rise to enhance permanent magnet properties (saturation magnetization, coercive field, energy product). the magnetic properties of thin films were found to be convenient for nanomagnet applications. (C) 2017 Elsevier B.V. All rights reserved.

Kaynak

Thin Solid Films

Cilt

625

Bağlantı

https://doi.org/10.1016/j.tsf.2017.01.050
https://hdl.handle.net/11436/2174

Koleksiyonlar

  • Enerji Sistemleri Mühendisliği Bölümü Koleksiyonu [117]
  • Scopus İndeksli Yayınlar Koleksiyonu [5931]
  • WoS İndeksli Yayınlar Koleksiyonu [5260]



DSpace software copyright © 2002-2015  DuraSpace
İletişim | Geri Bildirim
Theme by 
@mire NV
 

 




| Yönerge | Rehber | İletişim |

DSpace@RTEÜ

by OpenAIRE
Gelişmiş Arama

sherpa/romeo

Göz at

Tüm DSpaceBölümler & KoleksiyonlarTarihe GöreYazara GöreBaşlığa GöreKonuya GöreTüre GöreDile GöreBölüme GöreKategoriye GöreYayıncıya GöreErişim ŞekliKurum Yazarına GöreBu KoleksiyonTarihe GöreYazara GöreBaşlığa GöreKonuya GöreTüre GöreDile GöreBölüme GöreKategoriye GöreYayıncıya GöreErişim ŞekliKurum Yazarına Göre

Hesabım

GirişKayıt

İstatistikler

Google Analitik İstatistiklerini Görüntüle

DSpace software copyright © 2002-2015  DuraSpace
İletişim | Geri Bildirim
Theme by 
@mire NV
 

 


|| Rehber|| Yönerge || Kütüphane || Recep Tayyip Erdoğan Üniversitesi || OAI-PMH ||

Recep Tayyip Erdoğan Üniversitesi, Rize, Türkiye
İçerikte herhangi bir hata görürseniz, lütfen bildiriniz:

Creative Commons License
Recep Tayyip Erdoğan Üniversitesi Institutional Repository is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 4.0 Unported License..

DSpace@RTEÜ:


DSpace 6.2

tarafından İdeal DSpace hizmetleri çerçevesinde özelleştirilerek kurulmuştur.