Effect of two-pass friction stir processing on the microstructure and mechanical properties of as-cast binary Al-12Si alloy

Thumbnail

Göster/Aç

Full Text / Tam Metin (4.305Mb)

Erişim

info:eu-repo/semantics/closedAccess

Tarih

2015

Yazar

Aktarer, Semih M.
Sekban, Dursun Murat
Saray, Onur
Küçükömeroğlu, Tevfik
Ma, Zong Yi
Pürçek, Gençağa

Üst veri

Tüm öğe kaydını göster

Künye

Aktarer, S.M., Sekban, D.M., Saray, O., Kucukomeroglu, T., Ma, Z.Y., Purcek, G. (215). Effect of two-pass friction stir processing on the microstructure and mechanical properties of as-cast binary Al-12Si alloy. Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 636, 311-319. https://doi.org/10.1016/j.msea.2015.03.111

Özet

The effect of two-pass friction stir processing (FSP) on the microstructural evolution, mechanical properties and impact toughness of as-cast Al-12Si alloy was investigated systematically. Severe plastic deformation imposed by FSP resulted in a considerable fragmentation of the needle-shaped eutectic silicon particles into the smaller ones. the length of eutectic Si particles decreased from 27 +/- 23 mu m to about 2.6 +/- 2.4 mu m. the average aspect ratio of 6.1 +/- 5.1 for eutectic Si particles in the as-cast state decreased to about 2.6 +/- 1.0 after FSP with a corresponding increase in their roundness. the hardness, strength, ductility and impact toughness of the alloy increased simultaneously after two-pass FSP. the increase in the yield and tensile sirength values after FSP was about 20% and 29%, respectively. the FSPed alloy exhibited 25% elongation to failure and 15% uniform elongation which were almost seven times and five times higher, respectively, than those of the as-cast alloy. the hardness of the alloy increased from 58 Hv0.5 for the as-cast state to about 67 Hv0.5 after FSP. the absorbed energy during impact test increased to about 8.3 J/cm(2) after FSP, which is about seven times higher than that of the as-cast alloy. Improvements in all mechanical properties were mainly attributed to the radical changes of the shape, size arid distribution of the eutectic silicon particles along with the breakage and refined of the large alpha-Al grains during two-pass FSP. (C) 2015 Elsevier B.V. All rights reserved.

Kaynak

Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing

Cilt

636

Bağlantı

https://doi.org/10.1016/j.msea.2015.03.111
https://hdl.handle.net/11436/2807

Koleksiyonlar

  • Scopus İndeksli Yayınlar Koleksiyonu [6023]
  • Teknik Bilimler Meslek Yüksekokulu Koleksiyonu [201]
  • WoS İndeksli Yayınlar Koleksiyonu [5260]



DSpace software copyright © 2002-2015  DuraSpace
İletişim | Geri Bildirim
Theme by 
@mire NV
 

 




| Yönerge | Rehber | İletişim |

DSpace@RTEÜ

by OpenAIRE
Gelişmiş Arama

sherpa/romeo

Göz at

Tüm DSpaceBölümler & KoleksiyonlarTarihe GöreYazara GöreBaşlığa GöreKonuya GöreTüre GöreDile GöreBölüme GöreKategoriye GöreYayıncıya GöreErişim ŞekliKurum Yazarına GöreBu KoleksiyonTarihe GöreYazara GöreBaşlığa GöreKonuya GöreTüre GöreDile GöreBölüme GöreKategoriye GöreYayıncıya GöreErişim ŞekliKurum Yazarına Göre

Hesabım

GirişKayıt

İstatistikler

Google Analitik İstatistiklerini Görüntüle

DSpace software copyright © 2002-2015  DuraSpace
İletişim | Geri Bildirim
Theme by 
@mire NV
 

 


|| Rehber|| Yönerge || Kütüphane || Recep Tayyip Erdoğan Üniversitesi || OAI-PMH ||

Recep Tayyip Erdoğan Üniversitesi, Rize, Türkiye
İçerikte herhangi bir hata görürseniz, lütfen bildiriniz:

Creative Commons License
Recep Tayyip Erdoğan Üniversitesi Institutional Repository is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 4.0 Unported License..

DSpace@RTEÜ:


DSpace 6.2

tarafından İdeal DSpace hizmetleri çerçevesinde özelleştirilerek kurulmuştur.