Evaluation of structural and optical properties of Mn-Doped ZnO thin films synthesized by Sol-Gel technique

Thumbnail

Göster/Aç

Kapalı Erişim / Closed Access (617.1Kb)

Erişim

info:eu-repo/semantics/closedAccess

Tarih

2012

Yazar

Keskenler, Eyüp Fahri
Doğan, Seydi
Turgut, Güven
Gürbulak, Bekir

Üst veri

Tüm öğe kaydını göster

Künye

Keskenler, EF., Doğan, S., Turgut, G., Gürbulak, B. (2012). Evaluation of structural and optical properties of Mn-Doped ZnO thin films synthesized by Sol-Gel technique. Metallurgical and Materials Transactions A-Physical Metallurgy and Materials Science, 43A(13), 5088-5095.

Özet

Undoped ZnO and Mn-doped ZnO (MZO) films with 0.25, 0.50, and 0.75 mol pct were synthesized onto glass substrates by sol-gel spin-coating technique, and the effects of Mn on structural, morphologic, and optical properties were investigated. the XRD results indicate that the films have wurtzite structure with polycrystalline nature. However, the dominant peak was (002) diffraction peak for all samples; other diffraction peaks with less intensity such as (100), (101), (102), (110), (103), (112), and (004) were observed for the undoped ZnO. the lattice parameter values of MZO thin films were lower than that of the undoped ZnO. Plane stress values indicated that the films had the tensile stress. A decrease in the grain sizes was observed with the increasing Mn mole percent. the optical transmission values were found to be 82 pct for the undoped ZnO and 80, 78, and 75 pct for the MZO with 0.25, 0.50, and 0.75 mol pct, respectively, at the wavelength of 405 nm. the optical band gap values decreased from 3.287 to 3.270 eV, the surface roughness values increased from 58.13 to 60.67 nm, Urbach energy values increased-a 18.3-meV difference in Urbach energy was observed-and in addition, the steepness parameters decreased with increasing Mn content from 0 to 0.75 mol pct.

Kaynak

Metallurgical and Materials Transactions A-Physical Metallurgy and Materials Science

Cilt

43A

Sayı

13

Bağlantı

https://doi.org/10.1007/s11661-012-1365-4
https://hdl.handle.net/11436/3408

Koleksiyonlar

  • MÜF, Elektrik-Elektronik Mühendisliği Bölümü Koleksiyonu [196]
  • Scopus İndeksli Yayınlar Koleksiyonu [5917]
  • WoS İndeksli Yayınlar Koleksiyonu [5260]



DSpace software copyright © 2002-2015  DuraSpace
İletişim | Geri Bildirim
Theme by 
@mire NV
 

 




| Yönerge | Rehber | İletişim |

DSpace@RTEÜ

by OpenAIRE
Gelişmiş Arama

sherpa/romeo

Göz at

Tüm DSpaceBölümler & KoleksiyonlarTarihe GöreYazara GöreBaşlığa GöreKonuya GöreTüre GöreDile GöreBölüme GöreKategoriye GöreYayıncıya GöreErişim ŞekliKurum Yazarına GöreBu KoleksiyonTarihe GöreYazara GöreBaşlığa GöreKonuya GöreTüre GöreDile GöreBölüme GöreKategoriye GöreYayıncıya GöreErişim ŞekliKurum Yazarına Göre

Hesabım

GirişKayıt

İstatistikler

Google Analitik İstatistiklerini Görüntüle

DSpace software copyright © 2002-2015  DuraSpace
İletişim | Geri Bildirim
Theme by 
@mire NV
 

 


|| Rehber|| Yönerge || Kütüphane || Recep Tayyip Erdoğan Üniversitesi || OAI-PMH ||

Recep Tayyip Erdoğan Üniversitesi, Rize, Türkiye
İçerikte herhangi bir hata görürseniz, lütfen bildiriniz:

Creative Commons License
Recep Tayyip Erdoğan Üniversitesi Institutional Repository is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 4.0 Unported License..

DSpace@RTEÜ:


DSpace 6.2

tarafından İdeal DSpace hizmetleri çerçevesinde özelleştirilerek kurulmuştur.